----  [求助]centrex 814是什么材料???  (http://nju520.com/bbs/dispbbs.asp?boardid=20&id=11134)
--  作者：ldb202020
--  发布时间：2007-10-25 10:04:44
--  [求助]centrex 814是什么材料???
请教各位:centrex 814是什么材料???它有何特点??
--  作者：潜水艇
--  发布时间：2007-10-26 8:57:02
--  
Density1.05 g/cc
Melt Flow9 g/10 min
Tensile Strength, Yield38.5 MPa
Elongation at Break40 %
Elongation at Yield3 %
Tensile Modulus2.1 GPa
Charpy Impact, Notched, Low Temp0.29 J/cm?
Charpy Impact, Notched3.25 J/cm?
CTE, linear 20?C99 ?m/m-?C
Deflection Temperature at 0.46 MPa (66 psi)89 ?C
Deflection Temperature at 1.8 MPa (264 psi)77 ?C
Vicat Softening Point94 ?C
Flammability, UL94HB
Melt Temperature250 ?C
Mold Temperature60 ?C
Injection Velocity200 mm/sec
Injection Pressure60 MPa
--  作者：ldb202020
--  发布时间：2007-10-26 19:47:01
--  

Melt Temperature
        

250 ?C
        

 

Mold Temperature
        

60 ?C
        

 

Vicat Softening Point
        

94 ?C
        

温度后面为何还有"?"不理解!

 

 

 

 

温度后面为何还有"?"不理解!请问国内有批量生产这种材料吗???
--  作者：潜水艇
--  发布时间：2007-10-30 9:40:12
--  

摄式度的0C,那个小o认不出,所以就是问号了

centrex是某公司的注册商标,你搜索下你可以找到,然后找亚太或者中国区的代理
--  作者：ldb202020
--  发布时间：2007-11-1 9:08:12
--  

谢谢你!